Tensile Stress, brk, Type I / 抗張程度,斷裂,類型I, 5 mm/min

90

MPa

ASTM D 638

Tensile Strain, brk, Type I / 拉伸伸長,斷裂,類型I, 5 mm/min

2.6

%

ASTM D 638

Tensile Modulus / 拉伸模量, 5 mm/min

6200

MPa

ASTM D 638

Flexural Stress, yld / 撓曲強(qiáng)度, 屈服 , 1.3 mm/min, 50 mm span

160

MPa

ASTM D 790

Flexural Modulus / 撓曲模量, 1.3 mm/min, 50 mm span

5800

MPa

ASTM D 790

Hardness，Rockwell / 洛氏硬度 L

106

–

ASTM D 785

Tensile Stress, break / 抗張程度,斷裂, 5 mm/min

97

MPa

ISO 527

Tensile Strain, break / 拉伸伸長,斷裂, 5 mm/min

2.5

%

ISO 527

Tensile Modulus / 拉伸模量, 1 mm/min

7070

MPa

ISO 527

Flexural Stress, yield / 彎曲強(qiáng)度,屈服, 2 mm/min

167

MPa

ISO 178

Flexural Modulus / 撓曲模量, 2 mm/min

6540

MPa

ISO 178

Izod Impact, unnotched / 無缺口懸臂梁沖擊, 23°C

650

J/m

ASTM D 4812

Izod Impact, notched / 懸臂梁缺口沖擊強(qiáng)度, 23°C

119

J/m

ASTM D 256

Izod Impact, notched / 懸臂梁缺口沖擊強(qiáng)度, -40°C

96

J/m

ASTM D 256

Instrumented IMPACT Total Energy / 裝有測量儀表的落鏢沖擊總能量, 23°C

22

J

ASTM D 3763

Izod Impact, notched / 懸臂梁缺口沖擊強(qiáng)度 80*10*4 +23°C

11

kJ/m2

ISO 180/1A

Charpy Impact, notched /簡支梁缺口沖擊強(qiáng)度, 23°C

11

kJ/m2

ISO 179/2C

HDT（熱變形溫度）, 0.45 MPa, 3.2 mm, unannealed （未退火）

140

°C

ASTM D 648

HDT（熱變形溫度）, 1.82 MPa, 3.2mm, unannealed （未退火）

135

°C

ASTM D 648

HDT（熱變形溫度）, 0.45 MPa, 6.4 mm, unannealed （未退火）

143

°C

ASTM D 648

HDT（熱變形溫度）, 1.82 MPa, 6.4 mm, unannealed （未退火）

137

°C

ASTM D 648

CTE（線形膨脹系數(shù)）, -40°C to 40°C, flow（流動）

2.89E-05

1/°C

ASTM E 831

CTE（線形膨脹系數(shù)）, -40°C to 40°C, xflow（橫向）

8.26E-05

1/°C

ASTM E 831

Vicat Softening Temp, Rate / 維卡軟化溫度，等級 B/50

143

°C

ISO 306

Vicat Softening Temp, Rate / 維卡軟化溫度，等級 B/120

146

°C

ISO 306

HDT（熱變形溫度）/Be, 0.45MPa Edgew 120*10*4 sp=100mm

143

°C

ISO 75/Be

HDT（熱變形溫度）/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm

137

°C

ISO 75/Ae

Relative Temp Index, Elec / 相對熱指數(shù)， 電性能

90

°C

UL 746B

Relative Temp Index, Mech w/impact / 相對熱指數(shù)，機(jī)械沖擊性能

90

°C

UL 746B

Relative Temp Index, Mech w/o impact / 相對熱指數(shù)，非機(jī)械沖擊性能

90

°C

UL 746B

Specific Gravity / 比重

1.2

–

ASTM D 792

Water Absorption / 吸水率, 24 hours

0.06

%

ASTM D 570

Mold Shrinkage / 收縮率, flow（流動）, 3.2 mm

0.2 – 0.5

%

SABIC Method

Melt Flow Rate / 熔流率,, 300°C/5.0 kgf

9

g/10 min

ASTM D 1238

Melt Volume Rate / 溶化體積流率, MVR at 300°C/5.0 kg

8

cm3/10 min

ISO 1133

Dielectric Strength, in oil / 耐電強(qiáng)度，在油中, 3.2 mm

16.5

kV/mm

ASTM D 149

Relative Permittivity / 相對介電常數(shù), 50/60 Hz

2.86

–

ASTM D 150

Dissipation Factor / 耗散因素, 50/60 Hz

0.0008

–

ASTM D 150

Arc Resistance, Tungsten / 耐電弧性 {PLC}

7

PLC Code

ASTM D 495

Hot Wire Ignition / 熱絲引燃 {PLC)

4

PLC Code

UL 746A

High Voltage Arc Track Rate / 高電壓電弧起痕速率 {PLC}

4

PLC Code

UL 746A

High Ampere Arc Ign, surface / 高電流電弧引燃，表面 {PLC}

4

PLC Code

UL 746A

UL Recognized, 94HB Flame Class Rating / 阻燃等級 (3)

1.47

mm

UL 94

Oxygen Index / 極限氧指數(shù) (LOI)

26

%

ASTM D 2863

UV-light, water exposure/immersion / 紫外線暴露，耐水/浸漬

F1

–

UL 746C